LOCTITE 7113
Harmonization Code : 3506.91.90.99 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg ; Adhesives based on polymers of headings 3901 to 3913 or on rubber; Other ; Other
Main features
- Post-Applied Cyanoacrylate Activation
- Rapid Solvent Flash-Off
- 24-Hour On-Part Activity
Product Description
LOCTITE SF 7113 is a transparent, colorless, very-low-viscosity cyanoacrylate activator for post-application treatment of exposed adhesive outside the bondline. The sulfenamide active ingredient is carried in n-heptane and dries in 60 seconds or less at 20 deg C. Applied material remains active on the part for up to 24 hours under that condition. The activator accelerates cure of exposed cyanoacrylate fillets and supports fast handling with compatible adhesive systems. It is used in selected decorative, loudspeaker, coil, and ferrite assembly processes.
Key features
- Post-applied cure activation: The liquid treats exposed cyanoacrylate outside the bondline after adhesive placement.
- Rapid solvent flash-off: Drying time is 60 seconds or less at 20 deg C.
- Extended on-part activity: The treated surface remains active for up to 24 hours under the listed condition.
Applications / Suitable for
- Post-curing exposed cyanoacrylate fillets
- Decorative and jewelry assembly
- Loudspeaker, coil, and ferrite assembly
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Physical Properties
Physical Properties
General Properties
Additional Information
As-supplied / before-processing properties
Typical values and characteristics for the product before cure, application, or assembly.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Appearance | Transparent, colorless liquid | - | As supplied |
| Active ingredient | Sulfenamide | - | As supplied |
| Solvent | n-Heptane | - | Carrier |
| Specific gravity | 0.68 | - | 25 deg C |
| Viscosity | 0.4 | mPa s | 20 deg C |
| Drying time | <=60 | s | 20 deg C |
| On-part life | 24 | h | After application |