TEROSON 5510
Harmonization Code : 3506.10.00.00 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg
Main features
- Elastic Modified-Silane Bonding
- Fast Skin-Over Processing
- 2 mm Depth of Cure
Product Description
TEROSON® MS 5510™ BLACK is a one-component, moisture-curing modified silane polymer adhesive and sealant for elastic bonding and sealing across a range of substrates. The black homogeneous paste cures by reaction with atmospheric moisture to form an elastomeric thermoset material. It combines high strength, high elongation, high initial tack, sag resistance, and compatibility with suitable paint systems for interior and exterior applications.
Key features
- Elastic bonding and sealing: Delivers a flexible cured bond with high elongation for joints subject to movement.
- Moisture-curing, one-component system: Requires no mixing and develops functional strength in approximately 24 hours under normal conditions.
- Application-friendly formulation: Sag resistant, high in initial tack, compatible with suitable paint systems, and free of solvents, isocyanates, silicones, and PVC.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Physical Properties
Mechanical Properties
Thermal Properties
Additional Information
As-supplied / before-processing properties
Typical properties of the uncured material; values are reference data rather than guaranteed product specifications.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Technology | Flextec™ polymer | — | Uncured material |
| Chemical type | Modified silane polymer | — | Uncured material |
| Appearance | Black homogeneous paste | — | Uncured material |
| Components | One component | — | No mixing required |
| Specific gravity | 1.4–1.5 | — | At 25°C |
| Extrusion rate | 150–600 | g/min | Typical uncured-material property |
| Flow | ≤2.5 | mm | ISO 7390 |
| Viscosity | 150,000–240,000 | mPa·s | Cone and plate, 25°C; shear rate 10 s−1 |
| Skin-over time | 20–50 | min | 25 ± 2°C, 50 ± 5% RH |
| Flash point | >93 | °C | ASTM D3278, Setaflash closed cup; SDS value |
After-processing / final-state properties
Typical cured-material properties depend on the stated cure schedule, substrate, specimen, and test method.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Depth of cure | ≥2 | mm | After 24 hours |
| Shore hardness | 35–50 | Shore A | ISO 868; cured 7 days at 22°C and 50 ± 5% RH |
| Tensile strength | ≥1.5 | N/mm² | ISO 527-3; cured 7 days at 22°C and 50 ± 5% RH |
| Elongation at break | 376 | % | ISO 527-3; cured 21 days at 22°C and 50 ± 5% RH |
| Glass-transition temperature | −69 | °C | ISO 11357-2; cured 21 days at 22°C and 50 ± 5% RH |
| Nonvolatile content | 98 | % | ASTM D2369; cured 21 days at 22°C and 50 ± 5% RH |
| Lap-shear strength | 1.6 | N/mm² | ISO 4587; grit-blasted steel; cured 21 days at 22°C |
| Lap-shear strength | 1.7 | N/mm² | ISO 4587; glass; cured 21 days at 22°C |
| T-peel strength | 0.2 | N/mm | ISO 11339; aluminum; cured 21 days at 22°C |
| Impact strength | 2.7 | J | ISO 9653; aluminum; cured 21 days at 22°C |