PERMABOND 919
Harmonization Code : 3506.10.00.00 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg
Main features
- Up to 250 deg C Service
- 20-Second Fixturing Time
- MIL-A-46050C Type V Class 1 Approval
Product Description
Permabond® 919 Cyanoacrylate is an allyl-based, low-viscosity adhesive specifically engineered to meet high-temperature resistance requirements. While it cures rapidly at room temperature like traditional cyanoacrylates, it features a unique secondary curing mechanism activated by heat. Following a post-curing schedule, this 100% reactive, solvent-free adhesive can withstand extreme environmental temperatures up to 250°C (482°F).
Key features
- Extreme temperature resistance: Secondary thermal cure mechanism allows the bonded joint to resist temperatures up to 250°C (482°F).
- Fast setting: Delivers fixture handling times of under 20 seconds on steel, phenolic, and rubber substrates at room temperature.
- Low viscosity: The 2-6 cP viscosity is ideal for tight-fitting parts and post-assembly wicking with a maximum gap fill of 0.05 mm.
Applications / Suitable for
- Assemblies exposed to high-temperature environments (up to 250°C after post-cure)
- Bonding metals (steel, aluminum), plastics, and rubbers
- Military and aerospace applications requiring MIL-A-46050C Type V Class 1 approval
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Physical Properties
Mechanical Properties
Thermal Properties
Electrical Properties
Additional Information
As-supplied / before-processing properties
Typical properties; these values are not intended for use in preparing specifications.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Chemical Composition | Allyl cyanoacrylate | - | - |
| Appearance | Colorless | - | Liquid |
| Viscosity | 2-6 | cP | at 25°C (mPa.s) |
| Specific Gravity | 1.1 | - | - |
| Maximum Gap Fill | 0.05 | mm | (0.002 in) |
| Flash Point | 83 | °C | (181.4°F) |
After-processing / final-state properties
Typical properties; these values are not intended for use in preparing specifications.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Fixture/Handling Time | < 20 | seconds | Steel, Buna N Rubber, Phenolic |
| Full Strength | 24 | hours | - |
| Shear Strength | 20-22 | N/mm² | Steel (ISO 4587) (2900-3200 psi) |
| Impact Strength | 3-5 | kJ/m² | ASTM D-950 (1.4-2.4 ft-lb/in²) |
| Hardness | 85 | Shore D | ISO 868 |
| Coefficient of Thermal Expansion | 90E-6 | mm/mm/°C | - |
| Coefficient of Thermal Conductivity | 0.1 | W/(m.K) | - |
| Post-Cured Temperature Resistance | 250 | °C | (482°F) after thermal activation |