LOCTITE E-00CL
Harmonization Code : 3506.91.90.99 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg ; Adhesives based on polymers of headings 3901 to 3913 or on rubber; Other ; Other
Main features
- 1:1 Two-Component Epoxy
- 3.5-Minute Working Life
- Electrically Insulating Epoxy
Product Description
LOCTITE® EA E-00CL™ is a fast-setting, two-component clear epoxy adhesive formulated for general-purpose structural bonding, potting, and encapsulation applications. The adhesive cures at room temperature to form a clear, rigid, machinable bond line with excellent electrical insulation properties and resistance to a wide range of chemicals and solvents. It bonds effectively to metals, plastics, glass, ceramics, rubber, and wood, making it ideal for applications where a transparent bond line is required.
Key Features & Benefits
- Two-component clear epoxy adhesive system.
- Fast room-temperature cure after mixing.
- Low-viscosity formulation for easy dispensing.
- Clear, machinable cured bond line.
- Excellent electrical insulating characteristics.
- Good resistance to chemicals and solvents.
- Bonds metals, plastics, glass, wood, ceramics and rubber.
Recommended Applications
- General-purpose industrial bonding.
- Potting and encapsulation.
- Electrical insulation applications.
- Transparent bond line assemblies.
- Plastic, metal, glass and ceramic bonding.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Physical Properties
Additional Information
As-Supplied / Before-Processing Properties
| Property | Value | Unit | Condition |
|---|---|---|---|
| Technology | Epoxy | — | Two-component adhesive |
| Appearance (Resin) | Clear to Slight Yellow | — | Liquid |
| Appearance (Hardener) | Clear to Slight Yellow | — | Liquid |
| Mix Ratio (Volume) | 1 : 1 | Resin : Hardener | By volume |
| Mix Ratio (Weight) | 100 : 100 | Resin : Hardener | By weight |
| Resin Viscosity | 7,000 - 13,000 | mPa·s (cP) | 25°C |
| Hardener Viscosity | 2,200 - 4,500 | mPa·s (cP) | 25°C |
| Specific Gravity | 1.1 | — | Resin, Hardener and Mixed |
| Working Life | 3.5 | minutes | 25°C |
| Tack Free Time | 4 | minutes | 25°C |
After-Processing / Final-State Properties
| Property | Value | Unit | Condition / Method |
|---|---|---|---|
| Glass Transition Temperature (Tg) | 20 | °C | Cured at 25°C |
| Shore Hardness | 80 | Shore D | ISO 868 |
| Elongation | 13 | % | ISO 527-2 |
| Tensile Strength | 26 | N/mm² | ISO 527-2 |
| Dielectric Breakdown Strength | 16 | kV/mm | IEC 60243-1 |
| Lap Shear Strength (Aluminum) | ≥6.9 | N/mm² | ISO 4587, 2 h @ 65°C cure |
| Lap Shear Strength (Steel) | 15 | N/mm² | 5 d @ 22°C cure |
| Lap Shear Strength (Stainless Steel) | 13 | N/mm² | 5 d @ 22°C cure |
| Block Shear Strength (PVC) | 17 | N/mm² | ISO 13445 |
| Block Shear Strength (Glass) | 15 | N/mm² | ISO 13445 |