JNC PA-1210-034 | Insulating Polyacrylate Ink
Harmonization Code : 32159090 | Printing ink, writing or drawing ink, and other inks, whether or not concentrated or solid, specifically for those classified as other within that category
Main features
- UV Curable/ Solvent free
- High Insulation reliability for fine pitch devices
- Advance Sensors
Product Description
PA-1210-034 is a UV-curable, solvent-free polyacrylate insulating in, sets a new benchmark for high insulating reliability in fine pitch devices. Its specialized polyacrylate composition offers robust dielectric properties, creating an insulating layer that guarantees the utmost in reliability. Its tensile modulus of 1600 MPa, this ink augments mechanical stability, making it an excellent choice for applications requiring both electrical insulation and structural integrity. Also features a residual stress of 14 MPa and a coefficient of thermal expansion (CTE) of 91 ppm/K, ensuring compatibility with diverse materials and minimizing the risk of performance-altering mismatches.
Industry Applications:
Fine Pitch Electronics | Microfabrication| Advance Sensors
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Thermal Properties
Electrical Properties
Mechanical Properties
Chemical Properties
Physical Properties
Additional Information
| Properties | PA-1210-034 |
| Solids content (wt. %) | 100 |
| Viscosity (mPa's) @25℃ | 35 |
| Surface tension (mN/m) @23℃ | 31 |
| Printing methods | Inkjet |
| Curing | 2,000mJ/cm2 @ 365nm |
| Post-curing | 175℃ 60min |
| Volume resistivity (Ω*cm) | 1E+15 |
| Breakdown voltage (V/um) | 80 |
| Dielectric constant (1kHz) @1V | 3.1 |
| Tensile modulus (MPa) | 1600 |
| Elongation (%) | 4 |
| Residual stress (MPa) | 14 |
| 5% weight loss temp (℃) | 295 |
| CTE ( | 91 |
| Tg (℃) | 136 |
| Water absorbance (%) @23℃ | 0.4 |